GF98.00-P-4010Q Top Coating Overview

GF98.00-P-4010Q Top Coating Overview

Component Identification:

Model 209.3

Material:
^ Solvent-based base coat
^ Water-based base coat

Processing method:
^ Metallic finish:
1. ESTA application
2. Pneumatic application

^ Standard paints:
ESTA

Coat thickness:
^ 13 microm (±2 microm) with metallic finishes
^ 20 microm (±5 microm) with standard paints

Intermediate drying:
^ Base coat containing solvent:
2 to 3 min flash-off time at ambient temperature

^ Water-soluble base paint
3 min at 60 °C (intermediate drying), additionally 1.5 min IR

Function:
^ The base coat serves as the base for the color and creates the effect for metallic paints.
^ It has good adhesion properties to the substrate and for the subsequent clear varnish.

Material:
^ 1C clear varnish
^ 2C clear varnish

Processing method:
ESTA high-rotation method

Layer thickness:
40 to 45 microm

Stoving conditions:
130 °C, 22 min

Function:
^ optical properties: gloss, blending, effect formation
^ Weather resistance: gloss stability, light fastness, crack stability
^ High elasticity (stone chip protection).

Notes on clear varnish coat:
^ Base coat containing solvent: 1C clear varnish
^ Water-soluble base coat: 2C clear varnish

Component Identification:

Model 209.4

Material:
Water-based base coat

Processing method:
^ Metallic finish:
1 ESTA application
2 Pneumatic application

^ Standard paints:
ESTA

Coat thickness:
^ 13 (±2 microm) with metallic finishes
^ 20 (±5 microm) with standard paints


Intermediate drying:
Water-soluble base coat:
3 min at 60 °C

Function:
^ The base coat serves as the base for the color and creates the effect for metallic paints.
^ It has good adhesion properties to the substrate and for the subsequent clear varnish.

Material:
2C clear varnish

Processing method:
ESTA high-rotation method

Coat thickness:
35 to 45 microm

Stoving conditions:
130 °C, 22 min

Function:
^ optical properties: gloss, blending, effect formation
^ Weather resistance: gloss stability, lightfastness, crack stability
^ High elasticity (stone chip protection).